Heterophasic Copolymer
PROPERTIES | TEST METHOD | UNIT | VALUE |
Melt Flow Rate (230°C, 2.16kg) | ASTM D1238 | g/10min | 6 |
Density | ASTM D1505 | g/cm3 | 0.900 |
Flexural Modulus | ASTM D790 | MPa | 1400 |
Tensile Strenght @Yield | ASTM D638 | MPa | 26 |
Tensile Elongation @Yield | ASTM D638 | % | 9 |
Notched Izod Impact -4°F(-20°C ) | ASTM D256 | J/m | 70 |
Notched Izod Impact 73°C (23°C) | ASTM D256 | J/m | 170 |
Shore Hardness (Shore D) | ISO 868 |
| 68 |
Vicat Softening Point 10N | ASTM D1525 | °C | 152 |
HDT Under Load 66(0.45Mpa),Unannealed | ASTM D648 | °C | 95 |
Accelerated oven Ageing (302°F (150°C) | ASTM D3012 | Saat | 360 |
Values shown are averages & are not to be considered as product specifications.
Description:
EP440L is a medium heterophasic copolymer with improved mechanical properties balance. The product features high stifness and outstanding impact strength at low tempretures and is specfically designed for injection molding applications. In comparison with conventional copolymers with the same MFR and same rigidity, EP440L, exhibits 35% higher toughness. EP440L is suitable for a wide range of applications in the packaging, automotive and consumer goods industries. Typical applications include luggage, paint pails, buckets, containers, crates, batteries and larg toys.
Typical Application:
Packaging, automotive and consumer goods industries luggage, paint pails, buckets, containers, crates, batteries and large Toys.